Excavation and the digging of trenches could post danger and hazard to workers. It can also cause severe and costly damages to underground Electrical Cables, Telecommunication Optical Fiber Cable Networks and Gas Distribution System, Industrial and also the Domestic Water Piping System.
These have led to the development of the Warning Marker Plate. Manufactured from Polyvinyl Chloride, LITAFLEX uPVC Cable Cover Plate possesses high impact strength and complies with the International Standard.
Its superior quality deem excellent for the protection of Cables and Pipes installed underground. For example, the wide range of bright, luminous colours with embosses raised lettering, will certainly enable easy identification, and thereby effectively signal caution when digging trenches. In addition, the ingenious design of the Interlocking Device also allows continuous connection.
| |
PF 120 |
120 |
1.8 |
2000 |
0.75 |
PF 150 |
150 |
2.0 |
2000 |
1.00 |
PF 200 |
200 |
2.0 |
1600 |
1.20 |
|
STANDARD LENGTH |
: |
1 Meter |
|
COLOUR |
: |
Yellow / Black |
|
|
Standard Embossing
|
|
DANGER |
 |
LT CABLE |
|
DANGER |
 |
HT CABLE |
|

|
| |
PA 120 |
120 |
1.8 |
2000 |
0.90 |
PA 150 |
150 |
2.0 |
2000 |
1.00 |
PA 172 |
172 |
2.0 |
1000 |
1.11 |
PA 272 |
272 |
2.0 |
1000 |
1.11 |
|
STANDARD LENGTH |
: |
1 Meter |
|
COLOUR |
: |
Yellow / Black |
|
|

|
| |
PS 200 |
200 |
2.0 |
25 |
1.64 |
|
STANDARD LENGTH |
: |
50 Meter Coil |
|
COLOUR |
: |
Yellow / Black |
|
|
 |
ASTM D1525 : 2007 Standard Test Method for Vicat Softening Temperature of Plastics |
|
|
Load (1kgf) Heat Transfer Medium (Silicone Oil) Heating Rate (50 +/- 5oC/hr) Vicat Softening Point, average |
|
88oC |
|
|
ONORM E6530 (CLAUSE 7.3) : 1985 Impact Strength (Drop Hammer Test)
Maximum Depth of Penetration of the 10kg drop Hammer Observation |
< 100mm : No crack |
|
ONORM E6530 (Clause 7.4) : 1985 Tensile Load of the longitudinal Connection Crosshead Speed (50mm/ min) |
|
|
Average Tensile Load prior to ageing Average Tensile Load after ageing Change in Tensile Load |
:1056N :1071N :1.4% |
|
|
Conditioning of Test Specimen ASTM D3045 : 1997 Practice for Heat Ageing of Plastics without Load Oven Temperature (70 + 2oC) Duration (168 hr)
|
|
|